Hot Rolled

This flat rolled steel produced from a slab which is put through the mill work rolls to determine the final thickness while at high temperatures.

Typical uses for Hot Rolled Steel

Automotive, truck frames, automotive wheels, pipes and tubular, water heaters, agriculture equipment, compressor shells, truck frames, railcar components, wheel rims, metal buildings, tippers, trailers, doors, shelving, wheel rims, discs, guard rails, pipe and tubular & automotive components

Formability

Hot Rolled Sheet is used for a wide range of applications, from simple bends to complex draws or structural applications that require a specific strength level. The steel grade and processing technique of the metal are important in order to meet the customer requirements.

Mechanical Properties

Properties	Grade A	Grade B	Grade C
>Y. S. (MPa) min <20mm 20-40mm >40mm	250 240 230	250 240 230	250 240 -
>U.T.S (MPa) min	410	410	410
>EI %(min) 5.65vA	23	23	23

Bend Test (IS 1599)

Thickness	Grade A	Grade B	Grade C
<25mm	3t	2t	2t
>25mm	3t	3t	2t

Impact Test (charpy V notch)*

Thickness	Temp.	Grade A	Grade B	Grade C
8-70mm	0 degree C	-	27J	-
8-32mm	-20 degree C	-	-	27J

Chemical Composition ( Product Analysis ) IS 2062

Grades	C (Max)	Mn (Max)	P (Max)	S (Max)	Si (Max)	A1 (Min)	Nb (Max)	V (Max)	Ti (Max)	CE (Max)
Grade A	0.23	1.50	0.035	0.035	0.30	0.02	-	-	-	0.42
Grade B	0.22	1.50	0.035	0.035	0.30	0.02	-	-	-	0.41
Grade C	0.20	1.50	0.035	0.035	0.30	0.02	-	-	-	0.39

*Average of three tests

Thickness Range
Grade A	8-150mm
Grade B	8-70mm
Grade C	8-32mm
Heat Treatment	Online Self Normalising
Inspection Agency	JSW / Customer / Other Inspection agencies
Remarks	Nitrogen content 90 PPM max.

HR Steel Grades for forming operations

Chemical composition (Product Analysis)

Grades	C (Max)	Mn (Max)	P (Max)	S (Max)	Si (Max)	A1 (Min)	Nb (Max)	V (Max)	Ti (Max)	CE (Max)
Fe 330	0.17	1.00	0.035	0.035	0.30	0.02	-	-	-	-
Fe 360	0.17	1.20	0.035	0.035	0.30	0.02	-	-	-	-
Fe 410	0.20	1.30	0.035	0.035	0.30	0.02	-	-	-	0.42
Fe 510	0.20	1.50	0.035	0.035	0.30	0.02		0.02 - 0.08 to be added in single / Combination**		0.45

Mechanical Properties

Properties	Fe330	Fe360	Fe410	Fe510
Y.S (MPa) min	205	235	255	355
U.T.S. (MPa)	330-440	360-470	410-520	510-620
EI % (min) 5.65vA	25	25	23	20

Bend Test (IS 1599)

Thickness	Fe330	Fe360	Fe410	Fe510
<12mm	1 t	1 t	2 t	2 t
>12-25mm	2 t	2 t	3 t	3 t

Impact Test (charpy V notch)*

Thickness	Temp.	Fe330	Fe360	Fe410	Fe510
12-25mm	0 degree C	27 J	27 J	27 J	27 J